  • Clad plate surfacing wire
    Clad plate surfacing wire

    Email:info@hkchuangwei.com

    • Details
    • Parameters


    復合板堆焊焊絲


    Model

    Specification (mm)

    Hardness (HRC)

    Main components

    Main uses and characteristics

    WD161

    2.42.8, 3.2

    58-65

    C:3.0-5.0

    Cr:22-27

    For single layer welding of wear-resistant plate, the hardness of single layer after welding can reach HRC60 or more.

    WD261

    2.42.8, 3.2

    57-63

    C:3.0-5.0

    Cr:22-27

    The hardness of double-layer welding for hardfacing of wear-resistant sheet can reach HRC60 or more after double-layer welding.It has better impact resistance and is not easy to fall off.

    WD361

    2.42.8, 3.2

    57-63

    C:3.0-5.0

    Cr:24-30

    For multi-layer surfacing of wear-resistant plate, the hardness of more than 3 layers is above HRC60.It has better impact resistance and is not easy to fall off.

    WD181

    2.42.8, 3.2

    58-65

    C:3.0-5.0

    Cr:22-27

    When the actual welding thickness is less than 3mm, the hardness after welding is above HRC60, which ensures good wear resistance.

    WD161H

    2.42.8, 3.2

    58-65

    C:3.0-5.0

    Cr:25-32

    The deposited metal after welding has high chromium content and good wear resistance. It is used for single layer welding.


    Products Recommended

    Aluminium Handle Wafer Butterfly Valve
    Stainless Steel Butterfly Valve
    DI Body Wafer Butterfly Valve
    Double Stem Wafer Butterfly Valve
    • Tel

      Tel+86 17725588382
    • Skype

    • Mail

    Click on the phone to make a call
    點擊電話進行一鍵撥打
    Click on the mailbox to send a key
    點擊郵箱進行一鍵發送
    婷婷五五月开心深爱网